FeCrAl Ferro-Chromium-Aluminum D A1 Tk1 Apm High-Temperature Heating Resistance Wire

Product Categories

Copper Nickel Alloy Wire [359]
Electric Resistance Wire [349]
Thermocouple Bare Wire [211]
FeCrAl Alloy [316]
Thermocouple Cable [249]
Nicr Alloy [469]
Thermal Spray Wire [220]
Furnace Heating Element [66]
Precision Alloy [341]
Copper Alloy [76]
Nickel Alloy [159]
Enamelled Wire [78]
High Temp Alloy [68]
Thermocouple Connector [30]

Shanghai Tankii Alloy Material Co.,Ltd

Trust Seal

Verified Supplier

Credit Check

Supplier Assessment

Contact Now

FeCrAl Ferro-Chromium-Aluminum D A1 Tk1 Apm High-Temperature Heating Resistance Wire

Name: FeCrAl FerroChromiumAluminum D A1 Tk1 Apm HighTemperature Heating Resistance Wire
Brand: TANKII
Price: 1 USD

Brand Name : TANKII

Model Number : APM

Certification : ISO， ROHS

Place of Origin : Shanghai China

MOQ : 10 KG

Price : Negotiation

Payment Terms : L/C,D/A,D/P,T/T,Western Union,MoneyGram

Supply Ability : 100 Tons/Month

Delivery Time : 25 days

Packaging Details : wooden Case

Material : TK APM

Resistivity : 1.45

Diameter : 0.05-10.0mm

Surface : Bright, Golden， Blue， oxidation etc.

sample : accepted small order

HS Code : 72230000

Shape : ribbon, round wire, flat wire, flat strip, rod, bar, pipe, tube,

Contact Now

This product takes refined master alloy as raw material, uses powder metallurgy technology to manufacture alloy ingots, and is manufactured by special cold and hot processing and heat treatment process. The product has the advantages of strong oxidation resistance, good corrosion resistance at high temperature, small creep of electro-thermal components, long service life at high temperature and small change of resistance. It is suitable for high temperature 1420 C, high power density, corrosive atmosphere, carbon atmosphere and other working environments. It can be used in ceramic kilns, high temperature heat treatment furnaces, laboratory furnaces, electronic industrial furnaces and diffusion furnaces.

(Wt%) Main Composition

	C	Si	Mn	Cr	Al	Fe
Min	-	-	-	20	5.5	Bal.
Max	0.04	0.5	0.4	22	6.0	Bal.

Main Mechanical Properties

Tensile Strength at Room Temperature	650-750MPa
Elongation Rate	15-25%
Hardness	HV220-260
Tensile Strength at 1000℃	22-27MPa
High Temperature Durability at 1000℃ and 6MPa	≥100h

Main Physical Properties

Density	7.1g/cm³
Resistivity	1.45×10^-6 Ω.m
Melting Point	1500℃
Maximum Continuous Working Temperature	1400℃
Resistance Temperature Coefficient(Ct)	800℃	1000℃	1400℃
Resistance Temperature Coefficient(Ct)	1.03	1.04	1.05
Average Linear Expansion Coefficient	20-800℃	20-1000℃	20-1400℃
Average Linear Expansion Coefficient	14	15	16

Fast life

1300℃

1350℃

Average Fast Life (Hours)

110

Sagging Rate After Rupture

Testing according to GB/T13300-91 standard method

FeCrAl Ferro-Chromium-Aluminum D A1 Tk1 Apm High-Temperature Heating Resistance Wire

Specifications

Wire diameter range φ0.1-10mm

Wholesale FeCrAl Ferro-Chromium-Aluminum D A1 Tk1 Apm High-Temperature Heating Resistance Wire from china suppliers

FeCrAl Ferro-Chromium-Aluminum D A1 Tk1 Apm High-Temperature Heating Resistance Wire Images

Inquiry Cart 0

Send your message to this supplier


*From:	Your email address is incorrect!
*To:	Shanghai Tankii Alloy Material Co.,Ltd
*Subject:	Subject is empty!
*Message:	For the best results, we recommend including the following details: -Self introduction -Required specifications -Inquire about price/MOQ Characters Remaining: (0/3000) Please enter 20 to 3000 characters to contact this supplier!